However, it is not a universal solution. For thick coatings, textured surfaces, or high-performance linings, Part 2 (pull-off) should be used. Used within its limits, ISO 16276-1 is one of the most cost-effective and reliable field tests for coating adhesion on structural steel. ISO 16276-1:2007 – Corrosion protection of steel structures by protective paint systems – Assessment of, and acceptance criteria for, the adhesion/cohesion (fracture strength) of a coating – Part 1: Cross-cut test.
| Parameter | Requirement | |-----------|-------------| | | Between 5 °C and 40 °C (coating and steel). | | Relative humidity | ≤ 85% during testing. | | Substrate condition | Dry, clean, no condensation. | | Curing time | Paint must be fully cured as per manufacturer's data (field conditions often require ≥ 7 days for ambient-cured systems). | | Blade spacing | 1 mm for DFT ≤ 60 µm; 2 mm for DFT 61–120 µm; 3 mm for DFT 121–250 µm. | | Number of cuts | 6 parallel cuts in two orthogonal directions. | | Tape | Transparent pressure-sensitive tape, 25 mm width, peel strength 10 ± 1 N/25 mm. | 5. Classification of Results The standard adopts the 0–5 scale from ISO 2409 but adds mandatory photographic references for each class in the annex. pdf iso -16276-1
| Class | Description | Appearance of cut area | |-------|-------------|------------------------| | | Perfect adhesion | Edges completely smooth, no flaking. | | 1 | Very slight flaking | <5% of lattice area affected. | | 2 | Slight flaking | 5–15% affected. | | 3 | Moderate flaking | 15–35% affected. | | 4 | Severe flaking | 35–65% affected. | | 5 | Very severe flaking | >65% affected (or complete detachment). | However, it is not a universal solution